Liquid-quenched Alloys / Aus der Schmelze abgeschreckte Legierungen (Landolt-Börnstein: Numerical Data and Functional Relationships in Science and Technology - New Series / Condensed Matter) (Vol 19)

354 Pages·1991·5.91 MB·English

by  A.R. Ferchmin

Definitions, units and conversion factors
Units are given for the cgs/emu system and SI, for defining relations of the magnetiza-
tion, B = H + 4p M, B = m (H + M) and B = m H + M, respectively.
0 0
m = 4p(cid:215) 10–7 VsA–1m–1, A: molar mass, r : mass density.
0
Quantity cgs/emu SI
B G = (erg cm–3)1/2 T = Vs m–2
1 G ” 10–4 T
H 1 Oe = (erg cm–3)1/2 A m–1
1 Oe ” 103/4p A m–1
M B = H + 4p M B = m (H + M) B = m H + M
0 0
G A m–1 T
1 G ” 103 A m–1 4p(cid:215) 10–4 T
P P = MV P = MV P = MV
G cm3 A m2 V s m
1 G cm3 ” 10–3 A m2 4p(cid:215) 10–10 V s m
s s = M/r s = M/r s = M/r
G cm3 g–1 A m2 kg–1 V s m kg –1
1 G cm3 g–1 ” 1 A m2 kg–1 4p(cid:215) 10–7 V s m kg –1
s s = s A s = s A s = s A
m m m m
G cm3 mol–1 A m2 mol–1 V s m mol–1
1 G cm3 mol–1 ” 10–3 A m2 mol–1 4p(cid:215) 10–10 V s m mol–1
c P = c H P = c H P = c m H
0
cm3 m3 m3
1 cm3 ” 4p(cid:215) 10–6 m3 4p(cid:215) 10–6 m3
c c = c /V c = c /V c = c /V
V V V V
cm3 cm–3 m3 m–3 m3 m–3
1 cm3 cm–3 ” 4p m3 m–3 4p m3 m–3
c c = c /r c = c /r c = c /r
g g V g V g V
cm3 g–1 m3 kg–1 m3 kg–1
1 cm3 g–1 ” 4p(cid:215) 10–3 m3 kg–1 4p(cid:215) 10–3 m3 kg–1
c c = c A c = c A c = c A
m m g m g m g
cm3 mol–1 m3 mol–1 m3 mol–1
1 cm3 mol–1 ” 4p(cid:215) 10–6 m3 mol–1 4p(cid:215) 10–6 m3 mol–1
R , R r = R B + 4p RM r = R B + m RM r = R B + RM
0 s H 0 s s H 0 0 s s H 0 s s
W cm G–1 m3 C–1 m3 C–1
1 W cm G–1 ” 100 m3 C–1 100 m3 C–1